Patient care in the restorative clinic of a public dental school after COVID-19 lockdown

Aim: This study, with the aim of checking some of the changes in patients' daily habits and their reasons for needing restorative treatment was conducted at a public university immediately on return to attendance after the COVID-19 pandemic lockdown. Methods: This survey consisted of interviews held by applying 2 questionnaires to students and patients. A single researcher collected data in all the restorative dentistry clinics at the university after the return to face-to-face activities in the period between 02/02/2021 and 07/30/2021. Data obtained by means of the questionnaires were submitted to descriptive analysis. Results: Ninety (90) participants answered the patient questionnaire. When considering possible associations between being in social isolation or not, significant values were found for changed type of diet (p=0.0011), frequency of eating (p=0.011) and toothbrushing (p=0.034). Data about 417 restorations were collected and among the reasons for restorative intervention, 33.03% were restoration replacement, 31.87% treatment of primary caries and 24.40% of dental wear/non-carious lesions. Conclusion: Patients who isolated themselves during the pandemic tended to change their eating habits and frequency of oral hygiene. Toothache was the main reason for seeking dental treatment and the replacement of pre-existing restorations was the main reason for restorative treatments

Effect of the Mixture of Coffee or Chocolate to Milk in the Progression of Des-Remineralization of Tooth Enamel -An in Vitro Study

Objective:To evaluate if there is any interference when adding coffee or chocolate to cow milk in the enamel des-remineralization process (orange juice/saliva).Material and Methods:48 specimens of human enamel (4x4 mm) were included in acrylic resin, ground flat, polished and randomly divided into the following experimental groups (n = 8): G1-saliva, G2-orange juice, G3 orange juice / milk; G4-Orange Juice / Chocolate, G5-Orange Juice / Coffee + milk and G6-milk. Each group was immersed for 60 seconds on each solution proposed and then immersed for 30 minutes in saliva. This cycle was repeated 4 times. Prior to these cycles, the Knoop microhardness average of each specimen was obtained. After the challenges proposed, the final microhardness average was calculated. The values obtained from the difference between the initial and final microhardness were subjected to ANOVA followed by Tukey test (p <0,05).Results:The orange juice had the highest change in microhardness and statistically different from all other groups. The microhardness change was statistically similar in the groups submitted to orange juice followed by immersion in milk, in chocolate and in the mixture milk + coffee. The pure milk and saliva caused no change in surface hardness of enamel.Conclusion:Milk or the addition of chocolate and coffee to milk was able to produce aprotective effect of the enamel surface against an erosive challenge

Effect of mouthrinses with different active agents in the prevention of initial dental erosion.

Introduction: Hydrochloric acid (HCl) from the gastric juice is the only source of intrinsic acid, which can reach the oral cavity in cases of gastroesophageal reflux or chronic vomiting, enhancing the risk of dental erosion. Aim: Compare the effects of mouthrinses with different active agents in the prevention of initial dental erosion caused by HCl. Subjects and Methods: Casein (CAS at 0.2%), sodium hexametaphosphate (HMP at 0.02%), titanium tetrafluoride (TiF4 at 0.34%), and stannous fluoride (SnF2 at 0.87%) were individually added to an experimental mouthrinse. The mouthrinse without additives was used as the negative control (C) and a commercially available mouthrinse for erosion (ELM – Elmex®) as the reference product. Enamel specimens were exposed to human saliva and randomly assigned to 6 experimental groups (n = 8). Specimens were submitted to erosion in HCl for 10 s, followed by to the experimental mouthrinses for 30 s, and artificial saliva for 60 min. This cycle was repeated 3 times. The total amounts of calcium and phosphorus released by the specimens in the 2nd and 3rd erosive challenges were evaluated by atomic emission spectrometry. Statistical analysis used Shapiro–Wilks and Hartley tests, followed by one‑way ANOVA and Tukey tests. Results: When compared with C, ELM and HMP presented significantly less calcium in solution, with no difference between them. All the groups showed similar and significantly less phosphorus than C, except CAS. Conclusions: HMP was the only agent that could match the protection against initial erosion of the commercially available mouthrinse in both analyses.

Supplementation of an Orange Juice with Dietary Proteins to Prevent Enamel and Dentin Erosion

Protein supplementation may be an alternative to reduce the erosive potential of acidic drinks. The aim of this in vitro study was to evaluate the erosive potential of an orange juice modified by dietary proteins. A commercially available orange juice was added 0.2 g/L casein, 2.0 g/L ovalbumin and their combination. The juice with no additives and a commercially available calcium-modified juice were used as negative and positive controls, respectively. Human enamel and dentin specimens (n=11) were tested in an erosion-remineralization cycling model. Enamel was analyzed by surface microhardness and profilometry, whilst dentin by profilometry only. Statistical analyses were performed using one-way ANOVA followed by Tukey's test (p<0.05). Calcium-modified juice showed the lowest erosive potential for both analyses (p<0.05). For enamel, the protein-added groups did not differ from each other (p>0.05) and showed significantly lower enamel loss compared to negative control (p<0.05). Regarding surface microhardness, casein showed the highest values compared to negative control (p<0.05). For dentin, none of the protein-added groups showed lower values of surface loss compared to negative control (p>0.05). In conclusion, for enamel the protein-modified orange juices presented reduced erosion of enamel, with casein showing a trend for better protection. For dentin, no reduction in the erosive potential was observed for the tested protein-modified orange juices.

A suplementação de proteína pode ser uma alternativa na redução do potencial erosivo de bebidas ácidas. O objetivo deste estudo in vitro foi avaliar o potencial erosivo do suco de laranja modificado por proteínas da dieta. A um suco de laranja disponível comercialmente foi adicionado 0,2 g/L de caseína, 2,0 g/L de ovalbumina e suas combinações. O suco sem aditivos, e um suco suplementado com cálcio foram utilizados como controles negativos e positivos, respectivamente. Espécimes de esmalte humano e de dentina radicular (n=11) foram testados em um modelo de ciclagem de erosão-remineralização. O esmalte foi analisado por microdureza de superfície e perfilometria, enquanto que a dentina, apenas por perfilometria. As análises estatísticas foram realizadas utilizando ANOVA um fator seguido pelo Teste de Tukey (p<0.05). O suco suplementado com cálcio mostrou o menor potencial erosivo para ambas as análises (p<0,05). Em relação ao esmalte, os grupos com adição de proteína não diferiram entre si (p>0,05) e mostraram significativamente uma menor perda de esmalte em relação ao grupo controle negativo (p<0,05). Para a microdureza, a caseína apresentou os maiores valores em relação ao controle negativo (p<0,05). Para a dentina, nenhum dos grupos com adição de proteína apresentou valores de perda de superfície menores quando comparados ao grupo controle negativo (p>0,05). Conclui-se que, para o esmalte os sucos de laranja modificados por proteínas apresentaram uma redução da erosão, com a caseína mostrando uma tendência para melhor proteção. Para a dentina, nenhuma redução da erosão foi observada para os sucos de laranja modificados por proteínas testados neste estudo.

Choice of toothpaste for the elderly: an in vitro study

Hyposalivation and dental root exposure in the elderly are problems that require special oral care. In this context, the characteristics of certain toothpastes are of particular importance. Thus, the aim of this study was to evaluate the cytotoxicity and dentin wear caused by seven different toothpastes. For dentin wear analysis, 40 root dentin specimens were submitted to 20,000 brushing cycles with the different toothpastes and distilled water (control group-CG), using a brushing machine. Dentin surface loss (SL) was measured by contact profilometer. The cytotoxicity of each toothpaste was tested using cultured fibroblasts submitted to a cell-culture-conditioned medium. Fresh medium served as the control. Cell viability was assessed by MTT assay after 24 h of contact with the conditioned media. The data were analyzed statistically by ANOVA, followed by Tukey’s test (p < 0.05). The SL of the CG was minimal and significantly lower than that of the Oral B Pro Health (OBPH) group (p < 0.05). All other groups presented SL in between that of the CG and the Oral B Pro Health OBPH group, except for the Sensodyne (SEN) group, which presented SL similar to that of CG (p = 0.05). The SEN group presented a percentage of viable cells similar to that of CG: between 60-89%. All the other toothpastes showed high cytotoxicity, with cell viability less than 50% of the CG. Considering study limitations, we concluded that only one of the seven tested toothpastes exhibited the most desirable toothpaste characteristics for the worldwide growing elderly population (e.g. low cytotoxicity and low-abrasive potential).

Lisura superficial de resinas compostas com nanopartículas após protocolos de acabamento e polimento / Smooth surface of nanoparticle composites after finishing and polishing protocols

O objetivo desse estudo foi avaliar a lisura de superfície de três resinas compostas por nanopartículas, após serem submetidas a três diferentes sistemas de acabamento e polimento. Foram obtidos 40 corpos de prova de cada resina (Filtek Z350 XT, Premise e Charisma Diamond) e distribuídos em quatro grupos experimentais (n=10): C (controle) - sem tratamento; SOF -Discos abrasivos Soflex; ENH - Pontas siliconadas Enhance e F/FF - Pontas diamantadas de granulação fina/extra-fina + disco de feltro e pasta diamantada. Após 24h da confecção e armazenamento, os sistemas de acabamento e polimento foram aplicados. A lisura superficial foi avaliada utilizando-se um rugosímetro, tendo sido realizadas cinco leituras em cada corpo de prova. A média dos valores de rugosidade de superfície [um] obtidos foi analisada através da ANOVA, dois fatores, seguido do teste de Tukey, com significância de 1%. Para todas as resinas testadas, houve diferença estatística entre os sistemas de acabamento e polimento testados (p<0,01). Para a resina Charisma, os valores de rugosidade foram: C - 0,10a; SOF - 0,24b; ENH - 0,23b; F/ FF - 0,32c. Para a Premisa: C-0,12a; SOF - 0,16ab; ENH - 0,22b; F/FF - 0,30<. Para a Filtek: C - 0,08'; SOF - 0,14ab; ENH - 0,20b<; F/FF - 0,26<. No grupo controle foram obtidos os melhores resultados de lisura de superfície para todas as resinas testadas. Em relação aos tratamentos, os grupos SOF e ENH promoveram as melhores lisuras de superfície, enquanto que o grupo F/FF resultou em superfícies com maiores rugosidades.

The aim of this study was to evaluate the smoothness surface of 3 composites by nanoparticles (Filtek Z350 XT, Premise e Charisma Diarnond], after being subjected to three different finishing and polishing systems. Were obtained 40 specimens of each resin selected and randomly divided into 4 experimental groups (n= 10): C (control) - no treatment; SOF - Abrasive discs Soflex; ENH - silicon tips Enhance; and F / FF - diamond tips fine/extra-fine granulation + felt disc and diamond paste. Twenty-four hours after the preparation and storage of the specimens in distilled water at 37°(, the finishing and polishing systems were applied. The smooth surface of the composites was evaluated using a rugosimeter, where five readings were taken on each specimen. The mean surface roughness (um) were analyzed by ANOVA, two factors, followed by Tukev's test, with significance of 1%. For ali resins tested, statistical difference was found between finishing and polishing systems tested (p<0,01). To the resin Charisma roughness values were: C - 0,10a; SOF - 0,24b; ENH - 0,23b; F/ FF - 0,32c. For the premise : C-0,12a; SOF - 0,16ab; ENH - 0,22b; F/FF - 0,30<. Para a Filtek: C - 0,08'; SOF - 0,14ab; ENH - 0,20b<; F/FF - 0,26<. The control group obtained better results of surface smoothness for ali composites tested. Regarding the treatments groups, SOF and ENH resulted on better smoothness surface, while the group FI FF resulted in surfaces with higher roughness.

The effect of milk ingestion after an orange juice in the superficial microhardness of human enamel: an in vitro study

Patients diet and habits are important factors that can determine the ocurrence of dental erosion. The objective of this study was to evaluate the ability of milk to reduce the erosion caused by orange juice in enamel. Specimens of human teeth were mbeddedd in acrylic resin, polished and submitted to the initial microhardness measurement (SMH) using a Knoop indenter with 25 g load for 10 seconds. The specimens with similar values of SMH were randomly divided into 4 experimental groups (n=10) according to the following treatments: C (Control): 30 minutes of immersion in artificial saliva; OJ: 1 minute of immersion in orange juice, followed by 30 minutes in artificial saliva; M: 1 minute of immersion in cow's milk followes by 30 minutes in artificial saliva; OJ + M: 1 minute of immersion in orange juice follwed by 1 minute in milk and 30 minutes of artificial saliva. These treatments were repeated for four times.The final SMH was determined and means of SMH values were calculated. Data were analyzed using ANOVA and Tukey's Test (p menor do que 0.05). The immerison of the specimens in milk after orange juice was able to reduce the surface softening caused by this acidic drink. It was concluded that milk after an erosive challenge may be an alternative to reduce enamel surface softening.

A ausência de radiopacidade em algunscimentos de ionômero de vidro / The absence of radiopacity of some glass ionomer cements

A radiopacidade é um pré-requisito imprescindível para materiais utilizados como base eforramento de restaurações. Possibilita que o profissional identifique a presença do material,permitindo a diferenciação com a estrutura dental adjacente. Objetivo: O objetivo desse estudofoi avaliar a radiopacidade de materiais de base e forramento disponíveis para uso clínico ecomparar com a radiopacidade do esmalte e dentina. Materiais e Métodos: Foram analisados:13 marcas comerciais de cimento de ionômero de vidro, 1 amálgama e 1 resina composta. Foramconfeccionados três corpos de prova com espessura de 1 mm para cada cimento de ionômerode vidro e para cada material restaurador. Obteve-se 1 espécime, com 1 mm de espessura, deesmalte/dentina através de um corte transversal da coroa dental. As tomadas radiográficas foramfeitas com o sistema digital ~VG 5000 Kodak e tempo de exposição de 0,32 segundos. Asimagens obtidas foram trabalhadas no programa Image Tool® obtendo-se os valores médiosde cinza. A análise estatística ANOVA, seguida pelo teste de Tukey (p 0,05) detectou diferençasconsideráveis. Resultados: Alguns cimentos de ionômero de vidro apresentaram radiopacidadeinferior à da dentina e inadequada segundo as normas ISO9917, sendo considerada insuficientepara um correto diagnóstico radiográfico. Conclusão: Conclui-se que existem cimentos de ionômerode vidro indicados como base e forramento de restaurações disponíveis para aquisiçãocom radiopacidade imprópria para serem detectados radiograficamente.

The radiopacity is an essential prerequisite for materiais used as a base liner and restorationsand allows the professional to identify the presence of the material allowing the differentiationfrom the adjacent tooth structure. Objectives: The aim of this study was to evaluate the radiopacityof base and liner materiais available for clinical use and compare to the radiopacity ofenamel and dentin. Materiais and methods: 13 glass ionomer cements, one resin composite andone amalgam were evaluated. Three specimens with 1 mm thickeness for each glass ionomercement and restorative material were prepared. Cross section was made from a third molardental crown to obtain enamel and dentin specimen with thickness of 1 mm. Radiographswere taken with digital system Kodak RVG5000 and exposure time of 0.32 seconds. The imageswere analysed through the programe Image Tool" to obtain the mean grey values. Statisticaltest ANOVA followed by Tukey test (p<0.05) detected considerable differences. Results: Someglass ionomer cements presented radiopacity lower than dentin, considered insufficient for acorrect radiographic diagnosis, according to ISO 9917. Conclusion: It was concluded that somebase and liner materiais available for purchase have an inadequaderadiopacity to be detectedradiographically.

Interaction between staining and degradation of a composite resin in contact with colored foods

Composite resins might be susceptible to degradation and staining when in contact with some foods and drinks. This study evaluated color alteration and changes in microhardness of a microhybrid composite after immersion in different colored foods and determined whether there was a correlation between these two variables. Eighty composite disks were randomly divided into 8 experimental groups (n = 10): kept dry; deionized water; orange juice; passion fruit juice; grape juice; ketchup; mustard and soy sauce. The disks were individually immersed in their respective test substance at 37 ºC, for a period of 28 days. Superficial analysis of the disk specimens was performed by taking microhardness measurements (Vickers, 50 g load for 45 seconds) and color alterations were determined with a spectrophotometer (CINTRA 10- using a CIEL*a*b* system, 400-700 nm wavelength, illuminant d65 and standard observer of 2º) at the following times: baseline (before immersion), 1, 7, 14, 21 and 28 days. Results were analyzed by ANOVA and Tukey's test (p < 0.05). Both variables were also submitted to Pearson's correlation test (p < 0.05). The passion fruit group underwent the greatest microhardness change, while the mustard group suffered the greatest color alteration. Significant positive correlation was found between the two variables for the groups deionized water, grape juice, soy sauce and ketchup. Not all color alteration could be associated with surface degradation.

Abrasion resistance of different resin composites / Resistência à abrasão de diferentes resinas compostas

Objective - This study evaluated the influence of toothbrushing and thermal cycling on surface roughness and weight alterations of four different composite resins. Methods - Five specimens of two nanofilled composites (Filtek Supreme and Esthet X), one submicron composite(spherical filler) (Palfique Estelite) and one microhybrid composite (irregular filler) (Filtek Z250/3M ESPE), were prepared according to the manufacturer's directions. Each specimen was thermal cycled 1,200 times and subjected to 40,000 toothbrushing cycles. At baseline and after thermal cycling and tootbrushing cycles, surface roughness and weight were determined. Results - After thermal cycling and toothbrush abrasion no statistically significant difference in weight was found, however, the Esthet X and Palfique Estelite showed decrease in weight while Filtek Supreme and Z250 showed increase in weight. The surface roughness increased after thermal cycling and toothbrushing (p<0.01). The spherical submicron filler (Palfique Estelite) showed the smoothest surface. Conclusion - According to the methodology applied in this study, all resins studied showed resistance to abrasion, however, Palfique Estelite after the tests showed the smoothest surface.

Objetivo - Este estudo avaliou a influência da escovação e alterações térmicas quanto às alterações superficiais de rugosidade e peso de quatro diferentes resinas compostas. Métodos - Foram empregadas duas resinas de nanopartículas (Filtek Supreme e Esthet X), uma microparticulada de partículas esféricas (Palfique Estelite) e uma microhíbrida de partículas irregulares (Filtek Z250). Foram preparados cinco corpos de prova para cada material de acordo com as instruções do fabricante. Cada corpo de prova foi ciclado 1.200 vezes e submetido a 40.000 ciclos de escovação. O peso e rugosidade da superfície foram determinados antes e após os ciclos térmicos e de escovação. Resultados - Esthet X e Palfique Estelite mostraram diminuição do peso enquanto que Filtek Supreme e Z250 apresentaram aumento, no entanto, não houve diferença estatisticamente significativa após ciclagem térmica e de escovação. A rugosidade superficial aumentou em todas as resinas compostas testadas após a ciclagem térmica e de escovação, sendo que a resina microparticulada de partículas esféricas (Palfique Estelite) apresentou ao final dos testes a superfície mais lisa (p<0.01). Conclusão - De acordo com a metodologia aplicada nesta pesquisa, todas as resinas compostas estudadas apresentaram resistência à abrasão, no entanto, a Palfique Estelite apresentou ao final dos testes a maior lisura superficial.

Degradação dos materiais restauradores utilizados em lesões cervicais não cariosas / Degradation of the restorative materials used in non-carious cervical lesions

OBJETIVO: Avaliar o efeito de bebidas ácidas e da escovação em materiais utilizados em lesões cervicais não cariosas. MÉTODOS: Três resinas compostas, um compômero e um cimento de ionômero resino-modificado foram testados. Para cada material, cinco espécimes foram imersos em uma das soluções teste (suco de laranja, coca-cola, uísque ou água destilada) por 10 dias a 37ºC. Em seguida, os espécimes foram submetidos à escovação (20000 ciclos, 200g de carga). O peso e a rugosidade superficial foram avaliados antes e após a imersão nas soluções e escovação. Os dados foram analisados pela ANOVA/Teste Tukey (p<0,05). RESULTADOS: As imersões em suco de laranja e coca-cola seguida de escovação causaram significativamente maior perda de peso para o compômero e cimento de ionômero de vidro resino-modificado comparado às resinas compostas. O maior aumento de rugosidade superficial foi observado no cimento de ionômero de vidro resino-modificado após imersão em suco de laranja seguida de escovação. CONCLUSÃO: A imersão em bebidas ácidas seguida de escovação causou degradação nos materiais restauradores avaliados, com perda de material e aumento na rugosidade superficial.

OBJECTIVE: Evaluate the effect of acidic beverages and brushing on the restorative materials used in non-carious cervical lesions. METHODS: Three composite resins, one compomer and one resin-modified glass ionomer were tested. Five specimens of each material were immersed in each of the test solutions (orange juice, Coca-Cola, whisky and distilled water) for a 10-day period at 37ºC. Next, the specimens were brushed (20000 cycles with a load of 200g). Weight and surface roughness were measured before and after immersion and brushing. The data were analyzed by ANOVA/Tukey Test (p<0.05). RESULTS: The compomer and resin-modified glass ionomer lost significantly more weight after immersion in orange juice and Coca-Cola followed by brushing than the composite resins. The resin-modified glass-ionomer presented the highest increase in surface roughness after orange juice immersion and brushing. CONCLUSION: Immersion in acidic beverages followed by brushing degraded the restorative materials tested, causing loss of material and increased surface roughness.

Sensibilidade dentinária e lesões não cariosas / Dentin sensitivity and non carious lesions

Os avanços tecnológicos na Odontologia e a maior preocupação da população com a saúde bucal conduziram a manutenção dos dentes por maiores períodos. A preservação dos dentes pode levar a perda de estrutura dental - lesões não cariosas - que com muita frequência é acompanhada de sensibilidade quando a dentina é exposta. Neste trabalho são abordados os seguintes temas: prevalência, características, fatores etiológicos, prevenção e tratamento. A sensibilidade pós- operatória também foi abordada. Respostas para questionamentos feitos por pesquisadores, professores, alunos, clínicos e pacientes foram os motivos que levaram às pesquisas apresentadas neste trabalho. Inicialmente, houve uma preocupação em se buscar a prevalência e características da sensibilidade através de pesquisas clínicas. De acordo com essas pesquisas, a prevalência de sensibilidade é alta, demonstrando a necessidade desses estudos. A etiologia da sensibilidade dentinária está diretamente relacionada com a ocorrência de lesões não cariosas, no entanto, somente algumas lesões não cariosas, ou alguns pacientes, desenvolvem sensibilidade. O embasamento da literatura e a experiência clínica deram um grande suporte para o entendimento deste problema e o desenvolvimento de projetos de pesquisa. Posteriormente, estudos in vitro foram desenvolvidos para se tentar elucidar a etiologia, a prevenção e o tratamento da sensibilidade dentinária e das lesões não-cariosas. A influência de alimentos ácidos e a abrasão por escavação: com diferentes cerdas de escova dental, dentifrícios e temperatura da água podem determinar a ocorrência destas lesões. Estudos empregando o laser de Nd:YAG mostraram-se promissores no tratamento da sensibilidade e como método preventivo da erosão dental. Em relação à sensibilidade pós-operatória, dois estudos, um in vitro e outro in vivo, empregando materiais desenvolvidos pela indústria para prevenção da sensibilidade pós- operatória de restaurações em resina composta foram elaborados. De acordo com esses estudos a técnica restauradora minuciosa e criteriosa, provavelmente, é o fator mais importante para se evitar a sensibilidade. Ao longo destes anos várias.

Due to the technological advances in the Dentistry field and the population's greater concern about oral health, it has been observed an increase in the longevity of the teeth in the mouth. This fact may lead to the loss of dental tissues- non carious lesions, which is frequently accompanied by sensitivity when dentin is exposed. In this thesis, the following topics were broached: prevalence, characteristics, etiological factors, prevention and treatment of dentin sensitivity and non carious lesions. Post operatory sensitivity was also mentioned. Overall, answers to questions posed by researchers, teachers, students, clinicians and patients were the reasons that led the researchers presented in this literature. Initially, there was a concern to check the prevalence and clinical characteristics of dentin sensitivity through clinical trials. According to these investigations, the prevalence of dentin sensitivity is thought to be high and strongly related to the presence of dental wear. The etiology of dentin sensitivity is strongly related to the presence of non carious lesions. However, not every dentin exposure or patient presents dentin sensitivity. The literature basement and clinical experience gave a great support to understand this problem and to develop research projects. Later, in vitro studies were conducted in order to elucidate the etiology, the prevention and treatment of dentin sensitivity and also, dental wear. The influence of acid foods and drinks and abrasion by brushing with different toothbrushes bristles, toothpastes and water temperature can determine the occurrence of such lesions. Studies using Nd:YAG laser have shown promising in the treatment of dentin sensitivity and as prevention of dental erosion. Regarding post operative sensitivity, two studies, one in vítro and another in vivo were conducted. Both studies tested commercially available products to reduce the sensitivity that may occur after composite restorations. According to these studies, an adequate and well executed restorative technique might be the most important factor to avoid sensitivity.

Effect of saliva contamination on the bond strength of an etch-and-rinse adhesive system to dentin / Efeito da contaminação salivar na resistência de união de um adesivo etch-and-rinse em dentina

Purpose: The aim of this study was to investigate the effect of saliva contamination on bond strength of an etch-and-rinse system to dentin. Methods: Fifty bovine incisors were embedded in acrylic resin and divided into 5 groups: G1 (control) - application of the adhesive system (Adper Single Bond 2 - 3M-ESPE); G2 - saliva contamination after acid etching of dentin, rinsing and drying; G3 - saliva contamination after acid etching of dentin and drying; G4 - saliva contamination after adhesive application, rinsing and drying; G5 - saliva contamination after adhesive application and drying. Contamination was performed by using 4 µL of simulated human saliva for 20 s. The adhesive system was applied according to the manufacturer's instructions; a composite resin was built as an inverted cone and was tested after 24 h at a cross-head speed of 0.5 mm/min. Results: When saliva contamination occurred after the adhesive photo-polymerization, bond strength was significantly reduced. The adhesive strength (MPa) mean values were: G1 = 18.1(±4.7) a; G2 = 20.5(±5.7) a; G3 = 17.3(±3.4) a; G4 = 12.6(±4.0) b; G5 = 9.8(±2.1) b (means followed by distinct letters are statistically different, P < 0.05). Conclusion: Saliva contamination negatively influenced bond strength of an etch-and-rinse adhesive, especially after the final polymerization of the adhesive system; in this condition, treatments were not efficient to recover adhesion.

Objetivo: Investigar o efeito da contaminação salivar na resistência de união de um adesivo condicione-e-lave em dentina. Metodologia: Cinquenta incisivos bovinos foram divididos em 5 grupos: G1 = (controle) aplicação do sistema adesivo (Adper Single Bond 2 - 3M-ESPE); G2 = contaminação com saliva após condicionamento ácido da dentina + lavagem e secagem; G3 = contaminação após o condicionamento ácido da dentina + secagem; G4 = contaminação com saliva após a aplicação do adesivo + lavagem e secagem; G5 = contaminação com saliva após a aplicação do adesivo + secagem. A contaminação foi realizada com 4 µL de saliva humana estimulada por 20 s. O sistema adesivo foi usado de acordo com as instruções do fabricante. A resina composta foi aplicada na forma de cone invertido, com o teste de tração realizado após24 h a 0,5 mm/min de velocidade. Resultados: As médias de resistência de união (em MPa): G1 = 18,1(±4,7) a; G2 = 20,5(±5,7) a; G3 = 17,3(±3,4) a; G4 = 12,6(±4,0) b; G5 = 9,8(±2,1) b, demonstrando que a resistência de união foi reduzida significativamente quando a contaminação salivar ocorreu após a fotopolimerização do adesivo. Conclusão: A contaminação influenciou negativamente a resistência de união do adesivo somente após a sua polimerização; nesta condição os tratamentos realizados não foram eficientes para recuperar a adesão.

The influence of water temperature during toothbrushing on root dentine: An in vitro study.

Background/Aims: The use of cold water during toothbrushing can cause dentine sensitivity and, to avoid this painful stimulus, some patients used to rinse their mouths with warm water when brushing. Thus, the objective of this study was to determine the effect of water temperature on the dental root surface during toothbrushing. Materials and Methods : Fragments of bovine dental roots were submitted to 15,000 strokes in a toothbrushing machine using a slurry of toothpaste/water, medium brushes, and a 200-g load. They were randomly divided into two groups: toothbrushing with cold water or with hot water. Tooth wear was measured by loss of weight and by tissue height. Statistical Analysis: The weight and height data obtained in 17 and 10 replicas respectively are presented as mean ± standard error of mean. The data were compared using the Kolgomorov-Smirnof (Lilliefors) test followed by one-way ANOVA. The level of significance was 5% (P < 0.05). Results: There were no significant differences between the two experimental groups. The mean percentages of weight losses were 5.61 ± 1.66 for cold water and 6.25 ± 1.98 for hot water. The mean dentine height losses were 51.02 ± 15.92 µm for cold water and 63.54 ± 17.75 µm for hot water. Conclusion: The use of warm water during toothbrushing promoted root dentine wear similar to that produced by the use of cold water. The results suggest that warm or cold water may be used during toothbrushing without any additional damage to the patients' dental hard tissues.

Avaliação in vitro da microdureza de novos compósitos em diferentes espessuras / In vitro microhardness evaluation of new composite resins in different thickness

Introdução - Com o surgimento de novos compósitos, há um grande interesse pelo conhecimento de suas propriedades mecânicas. O objetivo deste trabalho foi avaliar in vitro a microdureza Vickers de quatro compósitos (Z 250, Natural Look, Epricord e Clearfil Majesty), em espessuras de 0, 1, 2, 3 e 4 mm. Material e Métodos - Vinte corpos de prova para cada compósito foram confeccionados em matrizes circulares de polipropileno pretas e a resina inserida em porção única e fotopolimerizada por 40s. A seguir, foram armazenados por uma semana, a 37°C, a seco, em recipientes escuros. A microdureza Vickers foi avaliada por meio de um microdurômetro digital HMV (Shimatzu, Japão), com auxílio do software CAM-Wins, utilizando carga de 50gf por 45s. Cinco medidas foram obtidas por corpo de prova. A análise estatística utilizou o teste ANOVA e teste de Tukey, com um nível de significância de 5%. Resultados - Após a análise de variância observou-se diferença significante entre as resinas (F = 235,07), entre as espessuras (F = 331,10) e para a interação resina X espessura (F = 14,95). O valor de Tukey foi 12,12. Conclusões - Os valores de microdureza diminuíram com o aumento da espessura da resina composta, para todas as resinas utilizadas. A resina Z 250 possibilitou o seu uso em incrementos de até 3 mm, a Natural Look até 2 mm e as Epricord e a Clearfil Majesty até 1 mm apenas.

Introduction - Due to new dental composite resins are arising, there is a great interest in clarifying their mechanic's properties. The aim of this study was to investigate the in vitro microhardness of four composite resins (Z 250, Natural Look, Epricord and Clearfil Majesty) with different thicknesses 0, 1, 2, 3 and 4 mm. Material and Methods - Twenty specimens of each composite resin were made on matrices of black polypropylene with cylindrical holes in which a single portion of the resin was applied and photopolymerized for 40s. Following, they were stored for a week, at 37°C in a dry and dark chamber. Vickers microhardness was measured using a digital microdurometer HMV (Shimatzu, Japan) with the CAM-wins software, using 50gf for 45s.Five measurements were made for each specimen. The data were statistically analyzed using ANOVA and Tukey tests (p < 0.05). Results - After the analysis of variance, significant differences were detected among the composite resins (F = 235.07), among their thicknesses (F = 331.10), and between the resin x thickness interaction (F = 14.95). The Tukey value was 12.12. Conclusions - The results revealed that an increase of the resin thickness produced a decrease in microhardness, for all composite resins analyzed. Increments of composite resins should not exceed 3 mm for Z 250, 2 mm for Natural Look, and only 1 mm for Epricord and Clearfil Majesty.

A ação de gorduras alimentares na microdureza de uma resina composta fotopolimerizável / Effect of alimentary fats on microhardness of composite restoratives

Introdução - Este estudo in vitro teve como objetivo verificar se alguns alimentos gordurosos alteram a microdureza superficial de uma resina composta (Filtek Z250-3M Espe). Materia e Métodos - Vinte e cinco corpos de prova (4 mm de diâmetro x 2 mm de espessura) foram confeccionados e mantidos por 30 dias, em estufa, a 37°C e a seguir divididos aleatoriamente, em 5 grupos (n = 5). De acordo com os meios de imersão em que foram mantidos, por 21 dias a 37°C, os grupos foram definidos como: G1 - água deionizada (controle); G2 - maionese (Hellmans); G3 - banha (Sadia), G4 - óleo de soja (Soya); G5 - margarina (Doriana). A microdureza Vickers (HMW 2000 - Shimadzu) da superfície de cada corpo de prova foi avaliada, uma vez antes e a cada 7 dias após a imersão, usando 50 g de carga e 45 s de tempo. Os dados foram submetidos à análise estatística (ANOVA) e Tukey (p<0,05). Resultados - O resultados da ANOVA dois fatores (meios de imersão x tempos) para Delta Vickers mostraram que houve diferença estatisticamente significante para o fator meio de imersão (p = 0,02%), sendo que não há significância para o fator (p= 13,6%), bem como não há significância na interação deses fatores (p = 44,2%). Os valores de Delta Vickers para o fator meio de imersão encontrados foram: G1 (6,79a), G2 (18,31b), G3 (8,10a), G4 (8,70a), G5 (12,43ab). Conclusão - Todas as gorduras testadas alteraram significativamente a resina composta. Os grupos G2 e G5 apresentaram maior degradação. Não houve variação significativa para tempos

Streptococcus mutans-induced secondary caries adjacent to glass ionomer cement, composite resin and amalgam restorations in vitro

The aim of this study was to define, in vitro, the potential to inhibit secondary caries of restorative materials currently used in dental practice. Standard cavities were prepared on the buccal and lingual surfaces of fifty extracted human third molars. The teeth were randomly divided into five groups, each one restored with one of the following materials: glass ionomer cement (GIC); amalgam; light-cured composite resin; ion-releasing composite; and light-cured, fluoride-containing composite resin. The teeth were thermocycled, sterilized with gamma irradiation, exposed to a cariogenic challenge using a bacterial system using Streptococcus mutans, and then prepared for microscopic observation. The following parameters were measured in each lesion formed: extension, depth, and caries inhibition area. The outer lesions developed showed an intact surface layer and had a rectangular shape. Wall lesions were not observed inside the cavities. After Analysis of Variance and Component of Variance Models Analysis, it was observed that the GIC group had the smallest lesions and the greatest number of caries inhibition areas. The lesions developed around Amalgam and Ariston pHc restorations had an intermediate size and the largest lesions were observed around Z-100 and Heliomolar restorations. It may be concluded that the restorative materials GIC, amalgam and ion-releasing composites may reduce secondary caries formation.

O objetivo deste estudo foi definir, in vitro, o potencial de materiais restauradores, usados rotineiramente na prática clínica, na inibição da cárie secundária. Cavidades padronizadas foram preparadas nas faces vestibulares e linguais de 50 terceiros molares humanos extraídos. Os dentes foram divididos aleatoriamente em 5 grupos, cada um restaurado com um dos seguintes materiais: cimento de ionômero de vidro (CIV); amálgama; resina composta fotopolimerizável; compósito que libera íons, e resina composta fotopolimerizável contendo flúor. Os dentes foram termociclados, esterilizados com radiação gama, expostos a um desafio cariogênico utilizando um sistema bacteriano com Streptococcus mutans e preparados para observação microscópica. Os parâmetros medidos em cada lesão formada foram: extensão, profundidade e área de inibição de cárie. As lesões externas formadas apresentaram camada superficial intacta e formato retangular. Não foram vistas lesões de parede no interior das cavidades. Após Análise de Variância e Análise de Componentes de Variância, foi observado que o grupo CIV apresentou as menores lesões e o maior número de áreas de inibição de cárie. As lesões formadas ao redor das restaurações de amálgama e Ariston pHc apresentaram tamanho intermediário e as maiores lesões foram observadas ao redor das restaurações dos grupos Z-100 e Heliomolar. Pode ser concluído que os materiais restauradores CIV, amálgama e compósitos que liberam íons podem reduzir a formação de cáries secundárias.

Sensibilidade da dentina cervical: o efeito de algumas bebidas ácidas / Cervical dentin sensitivity: the effect of some acidic beverages

As bebidas ácidas podem causar erosão na superfície da dentina expondo e alargando seus túbulos, predispondo ao surgimento de hipersensibilidade dentinária. A identificação de elementos na dieta capazes de abrir túbulos dentinários é importante para a prevenção e tratamento dessa sensibilidade. Este estudo verificou as alterações micromorfológicas da su-perfície dentinária de dentes humanos em microscópio eletrô-nico de varredura (MEV), após a imersão em quatro diferentes bebidas ácidas, correlacionando o pH e a capacidade tampão com as alterações na superfície. Foram preparadas 20 amos-tras de dentina cervical. Essas amostras foram aleatoriamente divididas em cinco grupos (n=4): Controle (em água destilada); limão; maracujá; Coca-Cola® e vinho tinto. As amostras de todos os grupos foram imersas nas suas respectivas bebi-das durante 3 horas. A seguir, elas foram examinadas por MEV e fotografadas. O pH inicial e a titulação das bebidas ácidas foram obtidos. Todas as bebidas ácidas expuseram túbulos dentinários e aumentaram seu diâmetro. Assim, conclui-se gue, as bebidas ácidas estudadas são potencialmente capazes de desencadear hipersensibilidade dentinária. Os valores de pH e titulação obtidos, para cada bebida, não explicaram satisfatoriamente as alterações microscópicas encontradas.

Resistência de união de pinos de fibra de quartzo submetidos a diferentes tratamentos e fixados com cimentos resinosos / Quartz fiber posts tensile bond strength submitted to different treatments and fixed with resin cements

Avaliou-se a resistência de união à tração de dois tipos de pinos estéticos de fibra de quartzo Para Post (Coltène/Whaledent) e Light Post (Bisco) a dois cimentos resinos quimicamente ativados Para Post Cement (Coltène/Whaledent) e C&B Cement (Bisco). As superfícies de cimentação dos pinos foram limpas com álcool e então tratadas com ou sem microjateamento (microjateador Danville Engineering) e com ou sem silano (Monobond-S, Vivadent), a seguir foram utilizados dois adesivos: o Alloy Bond (SDI) ou o All Bond 2 (Bisco). Após a cimentação, os corpos-de-prova foram armazenados em água destilada a 37°C por 24 horas e, então, foram submetidos aos testes de união à tração no aparelho de ensaio mecânico (Instron). Embora tenha havido diferenças estatísticas significantes entre as variáveis estudadas, fica difícil destacá-las individulamente, pois os resultados variaram de acordo com as interações, não sendo possível estabelecer um padrão para essas cimentações.

Ação dos dentifrícios sobre a estrutura dental após imersão em bebida ácida – Estudo in vitro / Dentifrice effect on dental structure after immersion in acid beverage – In vitro study

O consumo de bebidas ácidas seguido de escovação pode causar grandes perdas de estrutura dental. Este estudo teve como objetivo avaliar o poder abrasivo de diferentes dentifrícios à dentina quando esta é submetida à imersão em suco de laranja. 70 segmentos de raízes bovinas foram divididos aleatoriamente em 10 grupos (n=7) em relação aos dentifrícios utilizados. G1: Sensodyne; G2: Controle (água destilada); G3: Sorriso Dentes Brancos; G4: Colgate Ação Total; G5: Close up Micropartículas; G6: Close up Liqui Fresh; G7: Phillips; G8: Colgate Controle do Tártaro; G9: Confident; G10: Tandy. Todos os grupos foram submetidos a 7.000 ciclos de escovação, sendo que a cada 1.000 ciclos foram imersos em suco de laranja por 90 s. Os dados iniciais e finais de peso e perfil foram obtidos em balança analítica e projetor de perfil respectivamente. Os resultados foram submetidos ao teste de Kruskal-Wallis. A maior perda de peso ocorreu no grupo G10 e a menor no G4, porém não se encontrou diferença estatisticamente significante entre os grupos. As maiores perdas de perfil ocorreram nos grupos G3, G6, G7, G10 sendo estatisticamente significante (p<0,05) em relação aos grupos G1, G2, G4, G5, G8, G9. A escovação com os dentifrícios Sorriso, Close up Liqui Fresh, Phillips e Tandy associada à bebida ácida produziram maior perda de estrutura dental.